Analysis of stress corrosion cracking in X80 pipeline steel: An approach from the Theory of Critical Distances

Abstract: This paper presents an analysis of Stress Corrosion Cracking (SCC) based on the Theory of Critical Distances (TCD). The research is based on an experimental program composed of fracture specimens with notch radius varying from 0 mm (crack-like defect) up to 1 mm, and tensile specimens. A pipeline steel was used in this work (X80). It has been analysed in one hydrogen embrittlement situation. The study has been completed with Finite Elements Simulation analysis. The capacity of the TCD to analyse SCC processes has been proven.

Otras comunicaciones del congreso o articulos relacionados con autores/as de la Universidad de Cantabria

Multi-wall carbon nanotubes do not necessarily improve the fracture behaviour of the epoxy matrix - Comunicación a Congreso
Effect of graphene on the fracture behaviour of 3D printed PLA SENB specimens - Comunicación a Congreso
Some thoughts about the application of the Master Curve methodology to ferritic steels containing notches - Comunicación a Congreso
Assessment of notched Polyvinyl chloride (PVC) tubular beams using the Theory of Critical Distances and Finite Element analysis - Comunicación a Congreso
FRACture mechanics TEsting of irradiated RPV steels by means of SUb-sized Specimens: FRACTESUS PROJECT - Comunicación a Congreso
Master curve evaluation of ANP-5 steel using mini-CT specimens - Comunicación a Congreso
Analysis of additively manufactured PLA containing notches using Failure Assessment Diagrams - Comunicación a Congreso
Environmental Fatigue Analysis of nuclear components within the framework of INCEFA-SCALE project - Comunicación a Congreso
Estimation of fracture loads in 3D printed PLA notched specimens using the ASED criterion - Comunicación a Congreso
FRACTESUS Project overview: objectives, organisation and initial findings - Comunicación a Congreso
Structural Integrity Evaluation of the "Constitución of 1812 bridge", over the Cádiz bay (Cádiz, España) - Comunicación a Congreso
Analysis of the environmental degradation effects on the cables of La Arena bridge (Spain) - Comunicación a Congreso
INCEFA-PLUS (Increasing safety in NPPs by Covering gaps in Environmental Fatigue Assessment) - Comunicación a Congreso
Analysis of environmentally assisted cracking processes in notched steels using the point method - Comunicación a Congreso
Methodology for the Structural integrity assessment of the "Constitución de 1812" Bridge, over the Bay of Cádiz (Cádiz, Spain) - Comunicación a Congreso
An extension of the Equivalent Material Concept applied to fracture of U-notched solids - Comunicación a Congreso
Fracture mechanics testing of irradiated RPV steels by means of sub-sized specimens: FRACTESUS project - Comunicación a Congreso
Graphene oxide does not seem to improve the fracture properties of injection molded - Comunicación a Congreso
Application of the Theory of the Critical Distances based methodology for the analysis of Environmentally Assisted Cracking processes in biomaterials - Comunicación a Congreso
Application of the incremental step loading technique to Small Punch Tests on S420 steel in acid environments - Comunicación a Congreso
The role of the testing rate on Small Punch tests for the estimation of fracture toughness in hydrogen embrittlement - Comunicación a Congreso
On the use of the combined FMC-ASED criterion for fracture prediction of notched specimens with nonlinear behavior - Comunicación a Congreso

Autoría: González P., Cicero S., Álvarez J.A., Arroyo B.,

Congreso: European Conference on Fracture (22º : 2018 : Belgrado)

Editorial: Elsevier B.V.

Año de publicación: 2018

Nº de páginas: 8

Tipo de publicación: Comunicación a Congreso

DOI: 10.1016/j.prostr.2018.12.002

ISSN: 2452-3216

Proyecto español: MAT2014-58738-C3-3-R

Url de la publicación: https://doi.org/10.1016/j.prostr.2018.12.002

Repositorio UCrea Leer publicación

Autoría

PABLO GONZALEZ GUTIERREZ

SERGIO CICERO GONZALEZ

JOSE ALBERTO ALVAREZ LASO

BORJA ARROYO MARTINEZ

Descargar referencia

Bib Ris